Type of resin (Gardner)(Sec) | Unsaturated Polyester Resin ISO Base |
Appearance | Clear Liquid |
Gel time | 10 - 15 min |
Gel time terms | Curing condition with 1 Gr. Co. (1%) and 2% MEKP (50%) |
Peak Temperature | Max 150 °C |
Solid Content | 67%±3 |
Viscosity at 25 C | 100 – 200 cP |
Acid Value | 25 – 35 mgKOH/g |
Shelf life | 6 Months |
Tensile Strength | 20 - 30 MPa (Test Method ISO 527-2) |
Elongation | 3% - 5% (Test Method ISO 527-2) |
Tensile modulus | 1100 MPa (Test Method ISO 527-2) |
Flexural Strength | 50 - 60 MPa (Test Method ISO 178) |
Flexural modulus | 1500 MPa (Test Method ISO 178) |
HDT | 35 - 40 °C (Test Method ASTM D648) |
Hardness | 20 - 25 Barcol (Test Method ASTM D2583) |
Wood coating (For In horizontal and vertical modes) |
Low colore | |
Good adhesion on wood surfaces | |
High activity | |
Strong hardness | |
Excellent drying | |
Appropriate viscosity |