Type of resin (Gardner)(Sec) | Unsaturated Polyester Resin Ortho Base / ISO Base |
Appearance | Clear Liquid |
Gel time | 1 - 3 Min |
Gel time terms | Curing condition with 1 Gr. CO (1%) and 1% TBPB (130 C°) |
Peak Temperature | Max 300 °C |
Solid Content | 65%±2 |
Viscosity at 25 C | 900 – 1400 cP |
Acid Value | 13 – 19 mgKOH/g |
Shelf life | 6 Months |
Tensile Strength | 50 - 70 MPa (Test Method ISO 527-2) |
Elongation | 4% - 6% (Test Method ISO 527-2) |
Tensile modulus | 1100 MPa (Test Method ISO 527-2) |
Flexural Strength | 120 - 135 MPa (Test Method ISO 178) |
Flexural modulus | 3100 - 3600 MPa (Test Method ISO 178) |
HDT | 110 - 130 °C (Test Method ASTM D648) |
Hardness | 40 - 50 Barcol (Test Method ASTM D2583) |
Volumetric Shrink | Max 1% (Test Method ASTM D2566) |
Producing SMC - BMC |
Medium viscosity | |
Good impact resistance | |
Good mechanical properties | |
Good chemical properties | |
Good hydrolysis resistance |