Type of resin (Gardner)(Sec) | Unsaturated Polyester Resin Ortho base - Thixotropic and containing accelerator |
Appearance | Clear Liquid / Blue Liquid |
Gel time | 14 - 25 min |
Gel time terms | ----- |
Peak Temperature | Max 190 °C |
Solid Content | 62% – 66 % |
Viscosity at 25 C | 450 – 650 cP |
Acid Value | 10 – 20 mgKOH/g |
Shelf life | 3 Month |
Tensile Strength | 55 - 70 MPa (Test Method ISO 527-2) |
Elongation | 3% - 10% (Test Method ISO 527-2) |
Tensile modulus | 460 - 1880 MPa (Test Method ISO 527-2) |
Flexural Strength | 100 - 130 MPa (Test Method ISO 178) |
Flexural modulus | 2450 - 3600 MPa (Test Method ISO 178) |
HDT | Min 55 °C (Test Method ASTM D648) |
Hardness | 37 - 45 Barcol (Test Method ASTM D2583) |
Volumetric Shrink | Max 1.3% (Test Method ASTM D2566) |
General purpose | |
Applications for the production of parts with high flexibility and low shrinkage | |
Hand Lay-up | |
Flotations Products (Tixotrop & Pre-Accelerator) | |
Artificial Stone | |
Paltrogens | |
Cooling Towers |
Low activity | |
Very good flexibility | |
Low Shrinkage | |
Good adhesion to fibers | |
Good mechanical properties | |
High impact resistance | |
Low water absorption |